The strength of structures depends not only on their shape but also on the materials and components from which they are made and the connections between them.


All materials can be described using comparisons such as their strength, durability, appearance and workability. All these material properties can be measured and tested but are also available in tables which can be referred to.


Designers and engineers must know the properties of the materials they use to ensure they will stand up to the intended purpose - otherwise the results can be disastrous!


__TOC__


=====Stress and Strain=====


[[File:ConcretePillars2.png|200px|right]]
The illustration shows two concrete pillars each with a compressive load applied to the end. It is difficult to know just by looking which of the two pillars is the most likely to break and so engineers need a way doing a fair comparison.


To even things out, engineers calculate how much load would be applied to each square metre of cross-sectional area and this is known as '''[[Stress]]'''. Many terms in engineering, science and mathematics are represented by Greek symbols and Stress is allocated the symbol '''σ ''(sigma)'''''.


In the case of the two pillars shown '''Stress = Load / Area = 500Nm<sup>2</sup>''' for the large pillar and '''400Nm<sup>2</sup>''' for the smaller one - so, surprisingly perhaps, it is the large one which might fail first because it is under the greatest Stress.


The pillars would also be squashed a little by the loads upon them - even concrete ones! The amount they are squashed ''(microscopically small in this case!)'' is used to calculate the '''[[Strain]]''' which is equal to the '''change in length divided by the original length''' and is allocated the Greek letter '''ε ''(epsilon)'''''.


=====Tensile Strength=====

[[File:TensileTest3.png|200px|right]]
A '''Tensile Test''' for thin sheet materials, such as paper, can be done by wrapping the ends of a sample around short pieces of dowel, gripping each end with strong fold-over type paper clips,  then loading with a 1kg mass as shown. The sample is progressively reduced in width, taking equal amounts from each side, until it can no longer support the mass. Different types of paper, for example, may be compared for strength - the strongest is the one bearing the 1kg load with least width.


Care must be taken to ensure the material is cut away leaving a smooth edge since any irregularities will create a '''[[Stress Concentration]]''' and cause the strip to break earlier than expected - try it! 


This is a simple '''Comparative Test'''. If a numerical result is required the cross-section of the thinned paper strip will need to be measured - ideally in square metres if '''[[S.I. Units]]''' are to used!


But this can be done - by using a [http://en.wikipedia.org/wiki/Micrometer '''Micrometer'''] for example, and/or measuring the thickness of, say, 100 sheets of paper then dividing by 100, etc..


=====Stress Concentration=====


[[File:StressConcentration2.png|300px|right]]
When materials are placed under stress care should be taken to ensure that all edges and surfaces are polished and smooth. Forces will concentrate around even the smallest surface imperfection causing the component to fail sooner than predicted by a theoretical calculation.


This can be catastrophic, as in the case of the [http://en.wikipedia.org/wiki/BOAC_Flight_781 '''Comet airliner disaster'''], or it can be an intended consequence, as in the case of a bar of chocolate for example.


Calculating the increase in '''[[Stress]] ''(σ<sub>max</sub>)''''' is very complex but for a simple scratch or indentation it can be estimated as follows:


[[File:StressConcentrationEquation.jpg|350px|right]] 

'''''Where:'''''
* '''''l''''' = length or depth of scratch
* '''''r''''' = the tip radius at the bottom of the scratch
* Capital '''I''' - '''[[Moment of Inertia]]''' for the material


The key point to note is that the best way to reduce the increase in '''[[Stress]]''' created by a scratch or cut is to increase the radius at the tip - and that is why drilling a hole at the end of a cut or tear can stop it spreading further! 


=====Tensile Test Rig===== 	


[[File:TensileTestRig.png |400px|right]] 
Data from which to calculate the '''[[Tensile Strength]]''' of stronger materials, can be obtained using the rig shown opposite.


Samples of thin line or wire may be gripped and stretched. As before, the load being applied divided by the cross-sectional area provides a value for the '''[[Stress|Tensile Stress]]''' being applied and any change in length divided by the original length will provide a value for '''[[Strain|Tensile Strain]]'''.


The maximum load the sample can withstand before breaking is known as the '''[[Tensile Strength|Ultimate Tensile Strength]] ''(U.T.S.)'''''  of the material.


=====Stress Strain Curve=====


[[File:StressStrainGraph1.png|300px|right]] 
The rig shown above is known as a [https://en.wikipedia.org/wiki/Tensometer'''Tensometer'''] and industrial devices are used to measure how much a material sample stretches under '''[[Stress]]''' to determine tensile properties of materials, such as '''[[Tensile Strength]]'''.


As the material sample is stretched, measurements of the Force applied are taken and divided by the cross-sectional area of the sample to provide the value for '''[[Stress]]'''. Similarly, the amount the sample stretches is divided by its original length to give a value for '''[[Strain]]'''.

The values for '''[[Stress]]''' and '''[[Strain]]''' can be plotted against each other to produce a curve as shown.


=====Hooke's Law and Young's Modulus=====


[[File:StressStrainGraph2.png|300px|right]] 
As material samples are stretched, initially the '''[[Stress]]''' is directly proportional to the '''[[Strain]]''' - producing the straight line as shown. The material is behaving in much the same way as a spring would under tension and, if the force is removed, the material returns to its original length. The material is obeying [http://en.wikipedia.org/wiki/Hookes_law '''Hooke's Law'''] and this phase is known as the '''Elastic Stage'''.


The '''[[Stress]]''' divided by the '''[[Strain]]''' during this '''Elastic Stage''' is a measure of the [https://en.wikipedia.org/wiki/Stiffness '''stiffness'''] of a material and is known as its '''[[Young's Modulus]]''' or [https://en.wikipedia.org/wiki/Elastic_modulus '''Modulus of Elasticity'''].


If a force is continued to be applied beyond this phase, the material reaches a point at which it stays permanently stretched. This is the '''Yield Point''' or '''Elastic Limit''' and beyond this, during its '''Plastic Stage''', the material will continue to remain permanently deformed until eventually it breaks.


Much can be determined about a material from its '''Stress/Strain Curve''' - for example, [http://en.wikipedia.org/wiki/Ductile '''Ductile'''] materials will exhibit an extended '''Plastic Stage''' whereas [http://en.wikipedia.org/wiki/Brittle '''Brittle'''] materials would have little or none at at all.

'''In short:'''
* a stiffer material will exhibit a steeper slope
* a brittle material will lack a plastic region
* a stronger material will show a higher UTS


=====Compressive Strength=====


[[File: CompressionTest2.png |450px|right]] 
This is a measure of the degree to which a material can withstand being squashed. It can be measured by squeezing a material sample and taking readings in a similar way to '''[[Tensile Strength]]''' to obtain figures for '''[[Stress|Compressive Stress]]''' and '''[[Strain|Compressive Strain]]'''.


Note that '''Compressive Strength''' is not the same as '''[[Tensile Strength]]''' and the values can be quite different.


As with materials in '''[[Tension]]''', materials under '''[[Compression]]''' will exhibit an elastic stage during which they obey [http://en.wikipedia.org/wiki/Hookes_law '''Hooke's Law'''] ''(e.g. a rubber ball will spring back into shape)'' and non-brittle material would then exhibit a '''Plastic Stage''' ''(e.g. a ball of wet clay would stay squashed)''.


But under compression, samples which are too long are more likely to '''[[Buckling|Buckle]]''' and very brittle materials may even explode!
----
<span style="color: red">'''Safety Point!'''
Always wear eye protection when testing materials!
</span>
----
Using a '''[[Engineers Vice|bench vice]]''' and '''[[Spanners_and_Wrenches#Special_Purpose_Spanners|Torque Wrench]]''',  a compression test can be done as a simple comparison - but the illustration shows how reading a value from the '''[[Spanners_and_Wrenches#Special_Purpose_Spanners|Torque Wrench]]''' can even provide a measurement.


The wrench will provide a value in '''[[newton|newtons]]''' x metres '''''(Nm)'''''. If we imagine the wrench to be 1 metre long we can see that, in effect, the reading in '''Nm''' is simply the force on the sample ''(in '''[[newton|newtons]]''')'' x the vice screw thread pitch (in metres) as follows: 


Since work in must equal work out ''(assuming 100% efficiency of the vice of course!)'' then '''Force x Distance ''(in)''''' = '''Force x Distance ''(out)'''''.


So the '''[[Spanners_and_Wrenches#Special_Purpose_Spanners|Torque Wrench]]''' reading '''''(N)'' x 2πr ''(in metres)''''' = the vice screw pitch ''(in metres)'' x resulting force ''(in '''[[newton|newtons]]''')'' on the sample. Divide this force by the cross-sectional area '''''(m2)''''' and a value for '''[[Stress|Compressive Stress]]''' can be found.


=====Trade off=====


The '''[[Young's Modulus]]''' is a fundamental property of the material and '''Heat Treatment''' processes such as [https://en.wikipedia.org/wiki/Annealing_%28metallurgy%29 '''Annealing'''] or [https://en.wikipedia.org/wiki/Work_hardening '''Work Hardening'''] - you simply change degrees of [https://en.wikipedia.org/wiki/Elasticity_%28physics%29 '''Elasticity'''] and [https://en.wikipedia.org/wiki/Plasticity_%28physics%29 '''Plasticity''']. The shape of the '''Stress/Strain Curve''' therefore changes but the area under it remains the same because the work done to fracture is constant.
----
<span style="color: blue">'''Activity:'''</span>
* <span style="color: blue">Try:</span>
** <span style="color: blue">the tensile testing rig with 1.5mm2 or 18swg samples of copper, aluminium or brass wire;</span>
** <span style="color: blue">the vice compression test rig above with some 20mm long samples of aluminium, copper and brass  8mm or 10mm diameter.</span>
* <span style="color: blue">Test the samples in their original state then anneal and test again to see the difference.</span>
----
Cross-sectional areas of wire are provided for [http://en.wikipedia.org/wiki/Electrical_wiring_in_the_United_Kingdom#Cable_types '''electrical conductors'''] but may have to be calculated from the diameter for other materials. This can be measured using a [http://en.wikipedia.org/wiki/Micrometer '''micrometer'''] or a [http://en.wikipedia.org/wiki/Standard_wire_gauge '''Standard Wire Gauge ''(swg)'''''] used and the diameter looked up in tables. 


Materials and sections should be chosen so that components are not stressed beyond the [http://en.wikipedia.org/wiki/Yield_Point '''Yield Point''']. In practice, the '''Working Stress''' is below this and is determined by the [http://en.wikipedia.org/wiki/Factor_of_safety '''Factor of Safety'''].


=====Bending Strength=====


[[File:BentBeam.png|300px|right]] 
When a beam is loaded and bent as shown, the inside of the bend is subjected to the maximum '''[[Stress|Compressive Stress]]''' and the outside the bend experiences the maximum '''[[Stress|Tensile Stress]]'''.


Since most materials fail under '''[[Tension]]''' before they fail by '''[[Compression]]''', the '''[[Bending Strength]]''' can be taken to be the same as the '''[[Tensile Strength]]'''.


=====Simple Bending Equation=====


The '''[[Simple Bending Equation]]''' applies to simply supported beams ''(and arches if the radius of curvature is greater than 10 times the depth)''


This equation can be used to check that a beam has sufficient '''[[Bending Strength]]''' to support a given load - since it is taken to be the same as '''[[Tensile Strength]] ''(σ)'''''
[[File:BendingEquation.png|100px|right]]

'''''Where:'''''
* '''M''' = the '''[[Bending Moment|Maximum Bending Moment]]'''
* '''σ''' = the '''[[Tensile Strength]]''' of the material ''(obtainable from tables or by experiment)''
* Capital '''I''' = the '''[[Moment of Inertia]]''' about the Neutral Axis ''(for a rectangular beam this is its breadth times the depth cubed divided by 12)''.
* '''y''' = the distance of the '''[[Neutral Axis]]''' from the maximum stress ''(for a uniform rectangular beam this is half the depth)''


=====Deflection of Centrally Loaded Beams=====


[[File:DeflectionCalc.png|300px|right]]
The equation opposite can be used to find how much a simply supported beam ''(length - '''L''')'' would deflect if it is loaded ''(with a weight '''W''')''  in the centre. ''(Note: this equation makes no allowance for self-weight)''


=====Deflection of Beams with a Distributed Load=====


[[File:DistributedLoadEquation.png |300px|right]]
The deflection equation for a distributed load, such as its self-weight,  is given opposite. It can be seen that this is equivalent to multiplying self-weight by 5/8ths then adding it to the centrally applied load in the equation above.


For each of the equations:
* '''W''' = Load
* '''L''' = length of beam
* '''E''' = '''[[Young's Modulus]]''' for the material used
* '''Capital I''' = '''[[Moment of Inertia]]''' of the beam cross section.


Equations for other loading conditions can be found in ''''Structures' by J.E.Gordon ''(ISBN  0 14 02.1961 7)'''''


[[Category:Structures and Environments]]
[[Category:Materials and Components]]
[[Category:Terminology]]